Hydrothermal Formation of Hydroxyapatite Layers on the Surface of Type-A Zeolite

Type-A zeolite evenly covered with hydroxyapatite thin layers was prepared using hydrothermal treatment at 120°C for 8 h under autogenous pressure. The hydroxyapatite needlelike nanocrystals, 100–200 nm in diameter and 30 nm in thickness, were grown under the reaction between discharged Ca²⁺ ions from type-A zeolite and PO₄³⁻ ions in (NH₄)₃PO₄ solution. The preferential orientations of the c -axis of hydroxyapatite crystals perpendicular to a zeolite surface were observed using transmission electron microscopy. The crystal structure of type-A zeolite was not destroyed under the reaction, but the surface morphology was changed only with complete covering of scaly hydroxyapatite particles.     

Transient analysis of the release and reduction of NOx using a Pt/Ba/Al2O3 catalyst

The release and reduction of NO_x in a NO_x storage-reduction (NSR) catalyst were studied with a transient reaction analysis in the millisecond range, which was made possible by the combination of pulsed injection of gases and time resolved time-of-flight mass spectrometry. After an O₂ pulse and a subsequent NO pulse were injected into a pellet of the Pt/Ba/Al₂O₃ catalyst, the time profiles of several gas products, NO, N₂, NH₃ and H₂O, were obtained as a result of the release and reduction of NO_x caused by H₂ injection. Comparing the time profiles in another analysis, which were obtained using a model catalyst consisting of a flat 5 nmPt/Ba(NO₃)₂/cordierite plate, the release and reduction of NO_x on Pt/Ba/Al₂O₃ catalyst that stored NO_x took the following two steps; in the first step NO molecules were released from Ba and in the second step the released NO was reduced into N₂ by H₂ pulse injection. When this H₂ pulse was injected in a large amount, NO was reduced to NH₃ instead of N₂.

A only small amount of H₂O was detected because of the strong affinity for alumina support. We can analyze the NO_x regeneration process to separate two steps of the NO_x release and reduction by a detailed analysis of the time profiles using a two-step reaction model. From the result of the analysis, it is found that the rate constant for NO_x release increased as temperature increase.     

Relationships between hydrogen donor abilities and chemical structure of aromatic compounds in terms of coal liquefaction

To obtain fundamental information about hydrogen transfer, the relationships between hydrogen donor ability and chemical structure of model compounds representing donor solvents is studied using gas chromatography,¹H n.m.r. and computing calculation methods. The order of the model compounds in terms of the ability as donor solvent to release hydrogen is: decalin < tetralin < 1,2-dihydronaphthalene < < 1,4-dihydronaphthalene. This trend closely correlates with the difference in binding energies of the hydroaromatic compounds and their radicals, determined by intermediate neglect of differential overlap (INDO) calculation. Electron spin resonance spectroscopy (e.s.r.) confirms that radical species are created after heat-treatment of the donor compounds. The ability of model compounds representing coal to accept hydrogen is assessed from a comparison of the¹H n.m.r. spectra. It is established that donor and acceptor efficacies are dependent upon chemical structure.     

Elastoplastic Finite Element Analysis and Strength Evaluation of Adhesive Butt Joints of Similar and Dissimilar Hollow Shafts Subjected to External Bending Moments

Stress distributions and deformation of adhesive butt joints are analyzed by an elastoplastic finite element method when the joints of similar and dissimilar shafts are subjected to external bending moments. The effects of the ratio of Young's modulus for the adherends to that for an adhesive and the effects of the adhesive thickness on the interface stress distribution are investigated. Joint strength is predicted by using the elastoplastic interface stress distributions. It is found that the singular stress at the edge of the interfaces increases with an increase of the ratio of Young's modulus. Measurement of strains in joints and experiments on joint strength were conducted. The numerical results are in fairly good agreement with the experimental results. It is observed that the joint strength for dissimilar shafts are smaller than those for similar shafts. A fracture of dissimilar adhesive up-bonded shafts occurred from the interface of the adherend with smaller Young's modulus. It is seen that joint strength increases as the adhesive thickness increases.     

Some characteristics of a sparged agitated vessel under foaming — Mechanical control of foaming —

Foam-breaking with a rotating disk mechanical foam-breaker (MFRD) was studied for a foaming system containing a diluted detergent solution in a laboratory sparged agitated vessel. The change of the foam-breaking capacity of the MFRD by varying the air sparge rate, the working volume and the impeller speed or the disk diameter was measured. Based on these measurements, empirical equations are presented for predicting the critical foam-breaking regions of the MFRD fitted with the agitated vessel. The operational range where foam-breaking with the MFRD can be carried out effectively and economically is also discussed.     

Prediction model of surface residual stress within a machined surface by combining two orthogonal plane models

The variation of surface residual stress within a machined surface layer caused by face turning was studied. The size of the tool’s corner radius and the feed rate affect residual stress. A process model using the finite element method is proposed and the mechanical effects of the corner radius and feed rate on a machined surface were discussed. When a tool with a small corner radius is used, surface residual stress perpendicular to the cutting direction becomes compression stress. As well, surface residual stress changes from tension to compression as the feed rate decreases. The process model consists of an orthogonal cutting simulation and an indentation-like simulation of a corner radius into a work piece surface. The simulated results show quantitative agreement with the residual stress measured experimentally. The integrity of the machined surface will be controlled more efficiently if the cutting conditions during finishing are determined with the proper consideration of the surface generating process.     

Evaluation of hydrogen absorption properties of Ti–0.2 mass% Pd alloy in fluoride solutions

The hydrogen absorption properties of Ti–0.2 mass% Pd (Ti–0.2Pd) alloy in 2.0% and 0.2% acidulated phosphate fluoride (APF) and neutral 2.0% NaF solutions (25 °C) has been evaluated by hydrogen thermal desorption analysis. During the early stage of immersion (120 h) in the 2.0% APF solution, the amount of absorbed hydrogen was lower than 500 mass ppm. A thermal desorption of hydrogen primary appearing with a peak at 500–600 °C and a broad desorption ranging from 100 to 400 °C were observed. In the 0.2% APF solution, the amount of absorbed hydrogen saturated at 100–200 mass ppm; the thermal desorption of hydrogen appeared with a single peak at 550 °C. In the 2.0% NaF solution, hydrogen absorption was negligible even after 1000 h of immersion, although corrosion pits were observed. The results of the present study suggest that the hydrogen absorption of Ti–0.2Pd alloy, as compared with commercial pure titanium, is suppressed in fluoride solutions.     

Novel process for cover glass with ideal stress distribution

Abstract — This paper proposes a new process to manufacture cover glass that overcomes a strength trade‐off between the face and the edge. In the process, alkali barrier films are deposited on glass faces before an ion exchange process in order to control face stress properties without inhibiting the edge strengthening. As a demonstration of the process, alkali‐alumino‐silicate glass sheets with sputter‐deposited SiO₂ films were chemically strengthened, and then their stress properties and strengths were investigated. As a result, thicker SiO₂ films cause lower face DOL (depth of strengthened layer), and it is observed that the faces have lower DOL than the edges. In strength tests corresponding to major fracture modes of smartphone cover glass, specimens with 80–100 nm films have more balanced face performance and better edge impact strengths than the no‐film specimen.     

Note: detection of micro-cracks in the interlayer dielectric film by the stress based light scattering method

A phenomenon was discovered wherein light scattering strength from cracks increases when tensile stress is applied to micro-cracks produced in the interlayer dielectric film by chemical mechanical polishing treatment. It is likely that the change in light scattering intensity occurs because a region of high stress concentration (region with high variation in index of refraction) is produced near the crack tip due to stress, thus forming a type of scatterer. With this method, it is possible to detect only scatterers which respond to stress, and thus, it is possible to classify and separately detect cracks and particles.